Nanoscale polarization relaxation and piezoelectric properties of SBN thin films

resumo

Randomly oriented Sr0.75Ba0.25Nb2O6 thin films have been deposited on Pt(111)/Ti/SiO2/Si substrates using a polymeric chemical route to study their peculiar nanopolar structures and local ferroelectric properties using piezoresponse force microscopy (PFM) technique. PFM images reveals grains with contrast among fully white and fully black, a clear indication of non-zero polarization in the SBN films far above T-m similar to 221 K. Asymmetries observed in local hysteresis loops recorded at different grains suggest an imprint effect in the studied films due to an internal build-in electric field. Some grains show asymmetric hysteresis loops while other grains show symmetric hysteresis loops. The origin of the imprint effect observed in the SBN films is discussed in terms of complex defects associated to oxygen vacancies. The experimental relaxation curves were fitted using the Kohlrausch-Williams-Watts function. The time constant tau increases from 404 to 977 ms as the magnitude voltage increases.

palavras-chave

STRONTIUM BARIUM NIOBATE; CAPACITORS

categoria

Engineering; Physics

autores

Melo, M; Araujo, EB; Ivanov, M; Shur, VY; Kholkin, AL

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".