EFFECT OF Ni AND Cu INTERMEDIATE LAYERS ON THE SINTERABILITY OF A Ti-35SI-10MG (%AT.) MIXTURE SYNTHESIZED BY MECHANICAL ALLOYING

resumo

A Ti-35Si-10Mg (at.%) mixture was synthesized by mechanical alloying from Ti, Mg, and Si elemental powders. After milling the surface of the particles was chemically modified by the deposition of Ni and Cu thin layers by d.c. magnetron sputtering. Coated and uncoated particles were subsequently consolidated by two different routes: (i) cold isostatic pressing followed by pressureless sintering at T = 1300 degrees C in vacuum and (ii) cold isostatic pressing followed by hot isostatic pressing at T = 900 degrees C with an applied pressure of 1500 MPa. The results showed that all samples were formed by a final Ti(3)Si(5) + Mg(2)Si microstructure. Cu and Ni existed as single phases after hot isostatic pressing. Ni and Cu coatings acted as auxiliary sintering elements during compaction of the mechanically alloyed Ti-35Si-10Mg powders, giving rise to better final compacts. The higher values of hardness and Young's modulus were obtained for the HIP'ed coated samples, as result of their better densification.

palavras-chave

TI5SI3; CONSOLIDATION

categoria

Science & Technology - Other Topics; Materials Science

autores

Caetano, M; Oliveira, FJ; Silva, RF; Simoes, F; Trindade, B

nossos autores

agradecimentos

The authors gratefully acknowledge the financial support from Portuguese Foundation for Science and Technology (FCT) thought project POCI/CTM/57536/2004.

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".