Submicrometric NASICON ceramics with improved electrical conductivity obtained from mechanically activated precursors

resumo

Na3Si2Zr1.88Y0.12PO11.94 was for the first time synthesised using mechanically activated mixtures of (ZrO2)(0.97)(Y2O3)(0.03), Na(3)PO(4)(.)12H(2)O and SiO2 aiming to lower the sintering temperature thus improving chemical homogeneity. The best result was obtained with powder mixtures activated in Teflon containers with partial amorphisation of the reactants attained after milling for 70 h at a maximum of 300 rpm, without significant contamination. The microstructure consists of 300-500 nm agglomerates of smaller grains with size in the range 50-100 nm. Dense, single phase ceramics with submicrometric grain size were obtained from the activated mixture after sintering at 1050degreesC for 10 h. The ionic conductivity of these ceramics is 2.5 x 10(-3) S cm(-1) at room temperature, and 0.24 S cm(-1) at 300degreesC. These values are higher than those obtained with non-activated solid state reaction samples and amongst the highest reported in the literature. (C) 2004 Elsevier Ltd. All rights reserved.

palavras-chave

MECHANOCHEMICAL SYNTHESIS; SENSOR

categoria

Materials Science

autores

Fuentes, RO; Figueiredo, FM; Soares, MR; Marques, FMB

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".