Mechanosynthesis of La1-xSrxGa1-yMgyO3-delta materials

resumo

The room temperature mechanosynthesis of La1-xSrxGa1-yMgyO3-delta was demonstrated for a broad compositional range (x=0.05, y=0.10; x=0.20, y=0.20). This was achieved in atmospheric air with a planetary ball mill at 650 rpm in nylon containers rotating at 1300 rpm in the opposite direction. The maximum milling time was 360 min so that Zr contamination was kept below 0.25 mass%, as detected by ICP-AES. Powder X-ray diffraction revealed the formation of a perovskite phase since the early milling stages that becomes dominant in the patterns collected after milling for 360 min. The average crystallite diameter determined from XRD was ca. 30 nm, in good agreement with transmission electron microscopy observations. Ceramics with 93% of the theoretical density were obtained after sintering at 1300 degrees C. (c) 2008 Elsevier B.V. All rights reserved.

palavras-chave

DOPED LAGAO3; OXIDE; ELECTROLYTE; CONDUCTOR; LSGM

categoria

Chemistry; Physics

autores

Goncalves, P; Figueiredo, FM

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".