Glass-ceramic sealants for SOFC-based systems

resumo

The studies of electrochemical, physicochemical and mechanical properties of glass-ceramic sealants, based on SiO2-Al2O3-CaO-BaO and SiO2-MgO-BaO systems, showed sufficient stability in contact with zirconia, lanthanum gallate and ceria solid electrolytes at temperatures below 1100-1150 K. Thermal expansion of glass-ceramics can be optimized, to a considerable extent, by adding submicron powders of yttria-stabilized zirconia (YSZ). Excessive YSZ additions result, however, in increasing ionic contribution to the total conductivity, which is predominantly electronic. For moderately doped sealants, the conductivity is essentially composition-independent and varies in the range (2-7)x 10(-7) S/cm at 1123 K.

categoria

Electrochemistry; Energy & Fuels; Materials Science

autores

Kharton, VV; Tsipis, EV; Carvalho, AP; Kovalevsky, AV; Naumovich, EN; Marques, FMB; Frade, JR; Shaula, AL

nossos autores

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".