Electrophysical and thermomechanical properties of perovskites La(0.5)A(0.5)Mn(0.5)Ti(0.5)O(3-delta) (A = Ca, Sr, Ba) used as fuel cell anodes: the effect of radius of alkali-earth cation

resumo

The effect of the radius of the alkali-earth cation substituted into the A sublattice of La(0.5)A(0.5)Mn(0.5)Ti(0.5)O(3-delta) (D = DD degrees, Sr, Ba) perovskites on their stability and transport and thermomechanical properties is considered. The increase in the cation radius is shown to improve the phase stability and decrease the conductivity under both oxidative and reductive conditions. The thermal and chemical expansion of La(0.5)A(0.5)Mn(0.5)Ti(0.5)O(3-delta) ceramics is studied by dilatometry in controlled atmospheres and a wide temperature range at p(O-2)=10(-21)-0.21 atm. The coefficients of thermal expansion of La(0.5)A(0.5)Mn(0.5)Ti(0.5)O(3-delta) are in the interval of (10.7-14.3)x 10(-6) K-1, i.e., compatible with those of standard solid electrolytes of solid-oxide fuel cells. The maximum chemical expansion does not exceed 0.2% at isothermal reduction in the COaEuro'CO2 mixture.

palavras-chave

REACTION-MECHANISMS; ELECTRODE MATERIALS; CONDUCTIVITY; OXIDES; LACRO3; MN

categoria

Electrochemistry

autores

Kolotygin, VA; Ivanov, AI; Bredikhin, SI; Kharton, VV

nossos autores

Grupos

agradecimentos

This study was carried out with the financial support by the Ministry of Education and Science of the Russian Federation (contract no. 14.V25.31.0018) and the Russian Foundation for Basic Research (grant no. 13-03-12409).

Partilhe este projeto

Publicações similares

Usamos cookies para atividades de marketing e para lhe oferecer uma melhor experiência de navegação. Ao clicar em “Aceitar Cookies” você concorda com nossa política de cookies. Leia sobre como usamos cookies clicando em "Política de Privacidade e Cookies".